Remarkable enhancements in tensile strength (similar to 625 MPa) and elongation ratio (similar to 1%), being three and five times, respectively, as large as those of the binary Fe81Ga19 alloy, were obtained in situ dual-reinforcement (TaCparticle+TaCdendrite)/Fe81Ga19 magnetostrictive composites due to grain refinement and secondary-phase reinforcement.
- 出版日期2015-7-15
- 单位北京航空航天大学