The effect of metal transfer stability (spattering) on fume generation, morphology and composition in short-circuit MAG welding

作者：de Meneses Valter Alves; Pereira Gomes Joao Fernando; Scotti Americo^*

来源：Journal of Materials Processing Technology, 2014, 214(7): 1388-1397.

DOI：10.1016/j.jmatprotec.2014.02.012

• Welding
• Short-circuiting MAG
• Metal transfer stability
• Fume generation

The main objective of this work was to evaluate the hypothesis that the greater transfer stability leads also to less volume of fumes. Using an Ar + 25%CO2 blend as shielding gas and maintaining constant the average current, wire feed speed and welding speed, bead-on-plate welds were carried out with plain carbon steel solid wire. The welding voltage was scanned to progressively vary the transfer stability. Using two conditions of low stability and one with high stability, fume generation was evaluated by means of the AWS F1.2:2006 standard. The influence of these conditions on fume morphology and composition was also verified. A condition with greater transfer stability does not generate less fume quantity, despite the fact that this condition produces fewer spatters. Other factors such as short-circuit current, arcing time, droplet diameters and arc length are the likely governing factors, but in an interrelated way. Metal transfer stability does not influence either the composition or the size/morphology of fume particulates.

• 出版日期2014-7