Microstructural evolution and the variation of tensile behavior after aging heat treatment of precipitation hardened martensitic steel

作者：Shin Jong Ho; Jeong JaeSuk; Lee Jong Wook^*

来源：Materials Characterization, 2015, 99: 230-237.

DOI：10.1016/j.matchar.2014.11.024

• Synchrotron X-ray diffraction
• Martensite
• Precipitation
• Strain hardening exponent

The effects of aging temperature on the microstructural evolution and the tensile behavior of precipitation hardened martensitic steel were investigated. Microscopic analysis using transmission electron microscope (TEM) was combined with the microstructural analysis using the synchrotron X-ray diffraction (XRD) to characterize the microstructural evolution with aging temperature. Peak hardness was obtained by precipitation of the Ni3Al ordered phase. After aging at temperature range from 420 to 590 degrees C, spherical Ni3Al precipitates and ellipsoidal M23C6 carbides were observed within laths and at lath boundaries, respectively. Strain hardening behavior was analyzed with Ludwik equation. It is observed that the plastic strain regimes can be divided into two different stages by a rapid increase in strain hardening followed by a comparatively lower increase. At the first strain hardening stage, the aged specimen exhibited higher strain hardening exponent than the as-quenched specimen, and the exponent in the aged specimen was not changed considerably with increasing aging temperature. It is revealed that the strain hardening exponents at the first and the second stages were associated with the Ni3Al precipitates and the domain size representing the coherent scattering area, respectively.

• 出版日期2015-1