2D to 3D transition of polymeric carbon nitride nanosheets

作者：Chamorro Posada Pedro; Vazquez Cabo Jose; Sanchez Arevalo Francisco M; Martin Ramos Pablo; Martin Gil Jesus; Navas Gracia Luis M; Dante Roberto C^*

来源：Journal of Solid State Chemistry, 2014, 219: 232-241.

DOI：10.1016/j.jssc.2014.07.036

• Carbon nitride
• THz-TDS
• Nanosheets
• 2D materials

The transition from a prevalent turbostratic arrangement with low planar interactions (2D) to an array of polymeric carbon nitride nanosheets with stronger interplanar interactions (3D), occurring for samples treated above 650 degrees C, was detected by terahertz-time domain spectroscopy (THz-TDS). The simulated 3D material made of stacks of shifted quasi planar sheets composed of zigzagged polymer ribbons, delivered a XRD simulated pattern in relatively good agreement with the experimental one. The 2D to 3D transition was also supported by the simulation of THz-TDS spectra obtained from quantum chemistry calculations, in which the same broad bands around 2 THz and 1.5 THz were found for 2D and 3D arrays, respectively. This transition was also in accordance with the tightening of the interplanar distance probably due to an interplanar pi bond contribution, as evidenced also by a broad absorption around 2.6 eV in the UV-vis spectrum, which appeared in the sample treated at 650 degrees C, and increased in the sample treated at 700 degrees C. The band gap was calculated for 1D and 2D cases. The value of 3.374 eV for the 2D case is, within the model accuracy and precision, in a relative good agreement with the value of 3.055 eV obtained from the experimental results.

• 出版日期2014-11