Neutron irradiation and high temperature effects on amorphous Fe-based nano-coatings on steel - A macroscopic assessment

作者：Simos N^*; Zhong Z; Dooryhee E; Ghose S; Gill S; Camino F; Savkhyildiz I; Akdogan E K

来源：Journal of Nuclear Materials, 2017, 489: 164-179.

DOI：10.1016/j.jnucmat.2017.03.030

The study revealed that loss of ductility in an amorphous Fe-alloy coating on a steel substrate composite structure was essentially prevented from occurring, following radiation with modest neutron doses of similar to 2 x 10(18) n/cm(2). At the higher neutron dose of similar to 2 x 10(19), macroscopic stress-strain analysis showed that the amorphous Fe-alloy nanostructured coating, while still amorphous, experienced radiation-induced embrittlement, no longer offering protection against ductility loss in the coating-substrate composite structure. Neutron irradiation in a corrosive environment revealed exemplary oxidation/corrosion resistance of the amorphous Fe-alloy coating, which is attributed to the formation of the Fe2B phase in the coating. To establish the impact of elevated temperatures on the amorphous-to-crystalline transition in the amorphous Fe-alloy, electron microscopy was carried out which confirmed the radiation-induced suppression of crystallization in the amorphous Fe-alloy nanostructured coating.

• 出版日期2017-6