Hybrid carbon fibre/nylon 12 single polymer composites

作者：Hine P J^*; Bonner M; Ward I M; Swolfs Y; Verpoest I; Mierzwa A

来源：Composites Part A: Applied Science and Manufacturing , 2014, 65: 19-26.

DOI：10.1016/j.compositesa.2014.05.020

• Hybrid
• Polymer-matrix composites (PMCs)
• Mechanical properties
• Mechanical testing

This paper describes the production and properties of hybrid single polymer composites made from co-mingled tows of carbon and oriented nylon 12 fibres using the Leeds hot compaction process. For 22% volume fraction of carbon fibres, a well consolidated UD sample was made at a temperature of 176 degrees C, 2 degrees C below the temperature at which major melting of the oriented PA12 fibres, and loss of molecular orientation, occurs. For braided cloth a higher temperature of 178 degrees C was required to give a good sample, which is too close to the melting point of the PA12 multifilaments. Reducing the carbon fraction to 13% allowed a well consolidated sample (braided cloth) to be made at a lower temperature of 175 degrees C, giving a wider temperature processing In tension the hybrid samples were found to fail in a brittle manner while in bending the behavior was ductile as long the molecular orientation was retained.

• 出版日期2014-10