A comparative study on structural and optical properties of ZnO and Al-doped ZnO thin films obtained by ultrasonic spray method using different solvents

作者：Gahtar Abdelouahab; Rahal Achour; Benhaoua Boubaker; Benramache Said^*

来源：Optik, 2014, 125(14): 3674-3678.

DOI：10.1016/j.ijleo.2014.01.078

• ZnO
• Al doped ZnO
• Thin films
• Solvent
• Ultrasonic spray technique

Transparent conducting ZnO and Al doped ZnO thin films were deposited on glass substrate by ultrasonic spray method. The thin films with concentration of 0.1 M were deposited at 350 degrees C with 2 min of deposition time. The effects of ethanol and methanol solution before and after doping on the structural, optical and electrical properties were examined. The DRX analyses indicated that ZnO films have nanocrystalline nature and hexagonal wurtzite structure with (1 0 0) and (0 0 2) preferential orientation corresponding to ZnO films resulting from methanol and ethanol solution, respectively. The crystallinity of the thin films improved with methanol solution after doping to (0 0 2) oriented. All films exhibit an average optical transparency about 90%, in the visible range. The band gaps values of ZnO thin films are increased after doping from 3.10 to 3.26 eV and 3.27 to 3.30 eV upon Al doping obtained by ethanol and methanol solution, respectively. The electrical conductivity increase from 7.5 to 15.2 (Omega cm)(-1) of undoped to Al doped ZnO thin films prepared by using ethanol solution. However, for the methanol solution; the electrical conductivity of the film is stabilized after doping.

• 出版日期2014