Magnetic and magneto-optical studies on Zn1-xCrxTe (x=0.05) films grown on glass substrate

作者：Soundararajan D; Mangalaraj D^*; Nataraj D; Dorosinskii L; Santoyo Salazar J; Riley M J

来源：Journal of Magnetism and Magnetic Materials, 2009, 321(24): 4108-4114.

DOI：10.1016/j.jmmm.2009.08.012

• ZnTe:Cr film
• Magnetic domains
• M vs. H curve
• Magneto-optical study

Zn1-xCrxTe (x=0.05) films were prepared by thermal evaporation onto glass substrates. X-ray diffraction (XRD) was used to determine the crystalline quality of the ZnTe:Cr film. Magnetic force microscopy (MFM) investigation has shown a non-uniform distribution of magnetic domains with an average size of 4 nm at room temperature. SQUID measurements have further shown that the non-uniform distribution of domains does not affect the room temperature ferromagnetism of this material. Electron spin resonance spectroscopy (ESR) was done to determine the Cr valence state in the ZnTe lattice. Magnetic circular dichroism (MCD) analysis was used to confirm the ZnCrTe phase contributing to the ferromagnetic behavior.

• 出版日期2009-12
• 单位中国计量科学研究院