Acid-base membranes of imidazole-based sulfonated polyimides for vanadium flow batteries

作者：Wang, Lie; Yu, Lihong^*; Mu, Di; Yu, Liwei; Wang, Lei; Xi, Jingyu^*

来源：Journal of Membrane Science, 2018, 552: 167-176.

DOI：10.1016/j.memsci.2018.02.003

• Sulfonated polyimide
• Acid-base membrane
• Imidazole ring
• Sulfonation degree
• Vanadium flow battery

Acid-base sulfonated polyimides (SPIs) with different ratios of sulfonic groups and imidazole rings were synthesized by a one-step method for vanadium flow batteries (VFBs). The chemical structures of the SPI acid-base membranes were characterized by FTIR and H-1 NMR spectroscopy. The various SPI acid-base membranes were tested in terms of their physicochemical properties, proton-to-VO2+ selectivity, and VFB single-cell performance. The proposed mechanism of proton-transport channel, formed by acid-base pairs in the interfacial zone, may enhance proton conductivity. The optimized SPI acid-base membrane with a 50% sulfonation degree (SPI50) showed lower VO2+ permeability (2.2 x 10(-7) cm(2) min(-1)) than that of the Nafion 115 membrane (20.2 x 10(-7) cm(2) min(-1)). In the rate performance (40-160 mA cm(-2)) test, coulombic efficiency (CE: 96.1-98.9%) and energy efficiency (EE: 74.3-90.1%) of the VFB with the SPI50 membrane were much higher than those of Nafion 115 membrane (CE: 88.7-94.3%, EE: 71.7-85.0%). Moreover, the VFB with the SPI50 acid-base membrane exhibited a stable battery performance over 400 charge-discharge cycles at 160 mA cm(-2). The results demonstrate that the SPI50 acid-base membrane is a promising alternative for VFB applications.

• 出版日期2018-4-15
• 单位深圳大学; 深圳职业技术学院; 清华大学