摘要
Novel microwave dielectric materials of ZnZrNb1.84Sb0.16O8 ceramics with high Q were prepared through a conventional solid-state route and investigated for the first time. The XRD patterns revealed that all the specimens exhibited a single phase with the wolframite structure of ZrZrNb2O8 sintered in the temperature range of 1200-1300 degrees C. The microwave dielectric properties of ZnZrNb1.84Sb0.16O8 ceramics were strongly dependent on the sintering temperature and relative density. Excellent microwave dielectric properties with high Q x f of 89, 400 GHz (at 7.357 GHz), epsilon(r) of 26.27, and tau(f) values of -56.99 ppm/degrees C could be obtained sintered at 1250 degrees C for 4 h.
- 出版日期2016-3
- 单位天津大学