摘要
The HASTELLOY (R) C-22HS (TM) alloy is a face-centered cubic (fcc), nickel-based, corrosion-resistant superalloy. In the present study, the low-cycle-fatigue behaviors of the alloy were examined by in situ neutron diffraction at room temperature. The fatigue parameters included a total strain range of Delta epsilon=2% and a strain ratio of R = -1 (R = epsilon(min)/epsilon(max), where epsilon(min) in and epsilon(max) are the applied minimum and maximum strains, respectively). The effect of cyclic deformation on the lattice strains was studied as a function of cyclic straining. The cyclic hardening and softening behaviors during fatigue is discussed in light of the relationship between the peak widths and lattice strains.
- 出版日期2007-11
- 单位Los Alamos