摘要
UV-blue light was obtained from a thin-film electroluminescence device using Gd3Ga5O12:Ag as a light-emitting layer, which was deposited by using electron-beam evaporation. The crystal composition and structure of Gd3Ga5O12:Ag were studied by x-ray powder diffraction, The Gd3Ga5O12:Ag has a photoluminescence emission which peaked at around 397 and 467 nm, which were attributed to the oxide vacancies and Ag+, respectively. The brightness of 32 cd/m(2) was obtained when an alternating voltage of 130 V at 1 kHz was applied.