Optimized, biaxially textured BaFe1.8Co0.2As2 thin films with an in-plane alignment of 1.7 degrees have been realized on high-quality IBAD-textured MgO-coated technical substrates utilizing additional Fe buffer layers. High critical current densities (J(c)) were achieved, comparable to films on single crystalline MgO (J(c) >= 1 MA cm(-2) at 4 K, self-field). Transmission electron microscopy investigations reveal a small number of c-axis correlated defects introduced by the MgO template.