New composites of ZnO-P2O5/Ni having PTC transition and high Seebeck coefficient

作者：Maaroufi A^*; Oabi O; Lucas B; El Amrani A; Degot S

来源：Journal of Non-Crystalline Solids, 2012, 358(23): 3312-3317.

DOI：10.1016/j.jnoncrysol.2012.09.003

• Composites
• Electrical properties
• Glass ceramics
• PTC devices
• Percolation

In this article, we report the electrical conductivity (sigma) and Seebeck coefficient (S) of ZnO-P2O5 matrix filled with conductive powder of nickel (Ni). The variation of sigma versus volume fraction of Ni showed a non-conducting to conducting phase transition at percolation threshold (28 vol. %). The change of S from high positive to negative values exhibits that this transition is accompanied by the passing of carrier charge from p to n type. On the other hand, the measurements of sigma and S as function of temperature, above the percolation threshold, showed a positive temperature coefficient (PTC) phase transition at T-c >= 400 K, linked with a high S = -5000 mu V/K, giving highest power factor PF = sigma.S(2 approximate to)2.10(-4) W m(-1) K-2. The temperature dependence of the volume expansion enabled to confirm that this transition is associated to the thermal volume variation in matrix. However, the temperature dependence of sigma below the percolation threshold showed two different mechanisms: thermally activated hopping behavior at high temperatures and Mott's variable range hopping (VRH) at low temperatures.

• 出版日期2012-12-1