Alumina-supported manganese oxide sorbent prepared by sub-critical water impregnation for hot coal gas desulfurization

作者：Wang Jiancheng; Liu Lianwei; Han Lina; Hu Yongfeng; Chang Liping; Bao Weiren^*

来源：Fuel Processing Technology, 2013, 110: 235-241.

DOI：10.1016/j.fuproc.2012.12.020

• Hot coal gas
• Manganese-based sorbent
• Sub-critical water impregnation
• Precursor
• Desulfurization

Manganese oxide was loaded on the surface of gamma-Al2O3 by sub-critical water impregnation using manganese acetate and manganese nitrate precursors to synthesize Mn(A) and Mn(N) sorbents for removing H2S from hot coal gas. Active component precursors present very obvious effect on the desulfurization capacity of sorbent. Mn(A, 11) sorbent with 11% Mn content in gamma-Al2O3 maintains a desulfurization efficiency of close to 100% over 480 min. However, it reduces to below 90% for Mn(N, 11) sorbent when the reaction lasts over 75 min. The characterizing results of fresh and used sorbents from different precursors using AAS, SEM, BET, Raman, XAS and XPS techniques show that the acidity and alkalinity of active component precursor solution greatly influences the loading rate, valence state and dispersion of manganese on gamma-Al2O3, which are the main properties for improving desulfurization performance of sorbents. The manganese loading rate of Mn(A) sorbent is much higher than Mn(N) sorbent. The better dispersion of manganese on gamma-Al2O3 and the higher Mn2+ and Mn3+ contents on the surface of sorbent afford the high desulfurization activity of Mn(A). Moreover, Mn(A, 11) performs well in removing H2S from hot gas at 400 degrees C after three desulfurization -regeneration cycles.

• 出版日期2013-6
• 单位Canadian Light Source; Saskatoon; 太原理工大学