Understanding structural defects in lithium-rich layered oxide cathodes

作者：Jarvis Karalee A; Deng Zengqiang; Allard Lawrence F; Manthiram Arumugam; Ferreira Paulo J^*

来源：Journal of Materials Chemistry, 2012, 22(23): 11550-11555.

DOI：10.1039/c2jm30575e

Planar defects in lithium-rich layered oxides were examined by aberration-corrected scanning transmission electron microscopy (STEM) to understand their formation. Planar defects were found to form during the transition of the transition metal layer from a disordered R (3) over barm state to a lithium-ordered C2/m state. This disorder-to-order transition resulted in three orientation variants, namely [100], [110], and [1 (1) over bar0]. The fundamental mechanism behind the observed defects is a shear of +/-b/3[010] on the (001) transition metal planes, which is equivalent to the point group operations lost during the disorder-to-order transition. These displacements also produced twins and single unit cells with P3(1)12 symmetry. Lithium-rich layered oxides with and without nickel show the presence of these three orientation variants.

• 出版日期2012