High-dielectric-constant and low-loss microwave dielectric in the (1-x)Nd(Zn(1/2)Ti(1/2))O(3)-xSrTiO(3) system with a zero temperature coefficient of resonant frequency

作者：Huang Cheng Liang^*; Tseng Ching Fang; Yang Wen Ruei; Yang Tung Jung

来源：Journal of the American Ceramic Society, 2008, 91(7): 2201-2204.

DOI：10.1111/j.1551-2916.2008.02434.x

High-dielectric-constant and low-loss ceramics in the (1-x)Nd(Zn(1/2)Ti(1/2))O(3)-xSrTiO(3) system have been prepared by the conventional mixed-oxide route and their microwave dielectric properties have been investigated. A two-phase system was confirmed by the X-ray diffraction patterns, the energy-dispersive X-ray spectrometer analysis, and the measured lattice parameters. Addition of SrTiO(3), having a much smaller grain size in comparison with that of Nd(Zn(1/2)Ti(1/2))O(3), could effectively hold back abnormal grain growth in the Nd(Zn(1/2)Ti(1/2))O(3) matrix. Evaporation of Zn at high temperatures caused an increase in the dielectric loss of the system. The temperature coefficient of resonant frequency increases with increasing SrTiO(3) content and tunes through zero at x=0.52. Specimens with x=0.52 possessed an excellent combination of microwave dielectric properties: epsilon(r)similar to 54.2, Q x f similar to 84 000 GHz, and tau(f)similar to 0 ppm/degrees C. It is proposed as a suitable candidate material for today's 3G passive components and small-sized GPS patch antennas.

• 出版日期2008-7