Conversion Kinetics of Cerium Oxide into Sodium Cerium Sulfate in Na2SO4-H2SO4-H2O Solutions

作者：Um Namil; Hirato Tetsuji^*

来源：Materials Transactions, 2012, 53(11): 1992-1996.

DOI：10.2320/matertrans.M-M2012827

• cerium oxide
• sodium cerium sulfate
• sulfuric acid
• conversion kinetics
• shrinking-core model

The conversion of cerium oxide (CeO2) into sodium cerium sulfate (NaCe(SO4)(2)center dot H2O) in Na2SO4-H2SO4-H2O solutions was studied at elevated temperatures using a batch-type glass reactor under atmospheric pressure. Sodium sulfate (Na2SO4) concentration, sulfuric acid (H2SO4) concentration and reaction temperature were chosen as dependent variables, and the effects of these three variables on the conversion of cerium oxide into sodium cerium sulfate in Na2SO4-H2SO4-H2O solutions were investigated. The conversion includes two chemical reactions: cerium oxide dissolution and sodium cerium sulfate synthesis. The experimental data showed that increases of sodium sulfate concentration and sulfuric acid concentration decreased the conversion rate, whereas the conversion rate increased with increasing reaction temperature. The conversion kinetics of cerium oxide into sodium cerium sulfate for these three variables was analyzed and the fitted equation to the experimental data was determined. The variations of rate constant in dissolution and synthesis with temperature obeyed the Arrhenius equation with activation energies of 120 and 200 kJ/mol, respectively. In addition, the rate constant of cerium oxide dissolution was a function of the sodium sulfate concentration and sulfuric acid concentration at N-0.3 and C-6.5, respectively, and for sodium cerium oxide synthesis at N-0.2 and C-4.3. [doi:10.2320/matertrans.M-M2012827]

• 出版日期2012-11