As-cast microstructures and solidification paths of the Nb-Si-Ti ternary alloys in Nb5Si3-Ti5Si3 region

作者：Li Yan; Li Chang Rong^*; Du Zhen Min; Guo Cui Ping; Zhao Xin Qing

来源：Rare Metals, 2013, 32(5): 502-511.

DOI：10.1007/s12598-013-0143-9

• Nb-Si-Ti ternary system
• Liquidus projection
• Microstructure
• Solidification path

The as-cast microstructures and solidification paths of the Nb-Si-Ti ternary alloys in the Nb5Si3-Ti5Si3 region were investigated. Since there exist some isomorphous compounds in the Nb5Si3-Ti5Si3 region, such as alpha Nb5Si3 with B3Cr5 prototype, beta Nb5Si3 with Si3W5 prototype, gamma Nb5Si3 with Mn5Si3 prototype, and Ti5Si3 with Mn5Si3 prototype, the primary solidification areas of these compounds were not typically indentified in previous experiments. In the present paper, the microstructure observation, the phase identification, and the composition measurement were performed using scanning electron microscopy (SEM), X-ray diffraction (XRD), and electron probe microanalysis (EPMA), respectively. No ternary compound is found. There exist three primary solidification areas, beta Nb5-x (Ti) (x) Si-3, alpha Nb5-x (Ti) (x) Si-3, and Ti5-x (Nb) (x) Si-3 in the Nb5Si3-Ti5Si3 region. Together with the literature-reported experimental data and optimization results, the liquidus projection of the whole Nb-Si-Ti ternary system is constructed, and totally ten primary solidification areas-diamond-Si, Nb1-x (Ti) (x) Si-2, Ti1-x (Nb) (x) Si-2, Ti1-x (Nb) (x) Si, Ti5-x (Nb) (x) Si-4, beta Nb5-x (Ti) (x) Si-3, alpha Nb5-x (Ti) (x) Si-3, Ti5-x (Nb) (x) Si-3, (Nb,Ti)(3)Si, and BCC-and nine transitional invariant reactions-L + Nb1-x (Ti) (x) Si-2 -> Ti1-x (Nb) (x) Si-2 + Si, L + Nb1-x (Ti) (x) Si-2 -> Ti1-x (Nb) (x) Si-2 + Ti5-x (Nb) (x) Si-4, L + Ti5-x (Nb) (x) Si-4 -> Ti1-x (Nb) (x) Si-2 + Ti1-x (Nb) (x) Si, L + beta Nb5-x (Ti)(5)Si-3 -> Nb1-x (Ti) (x) Si-2 + Ti5-x (Nb) (x) Si-4, L + beta Nb5-x (Ti) (x) Si-3 -> alpha Nb5-x (Ti) (x) Si-3 + Ti5-x (Nb) (x) Si-4, L + alpha Nb5-x (Ti) (x) Si-3 -> Ti5-x (Nb) (x) Si-3 + Ti5-x (Nb) (x) Si-4, L + alpha Nb5-x (Ti) (x) Si-3 -> beta Nb5-x (Ti) (x) Si-3 + Ti5-x (Nb) (x) Si-3, L + beta Nb5-x (Ti) (x) Si-3 -> Ti5-x (Nb) (x) Si-3 + (Nb,Ti)(3)Si, and L + (Nb,Ti)(3)Si -> Ti5-x (Nb) (x) Si-3 + BCC-are confirmed.

• 出版日期2013-10
• 单位北京大学