AC magnetic properties of the soft magnetic composites based on Supermalloy nanocrystalline powder prepared by mechanical alloying

作者：Neamtu B V^*; Geoffroy O; Chicinas I; Isnard O

来源：Materials Science and Engineering B-Solid State Materials for Advanced Technology, 2012, 177(9): 661-665.

DOI：10.1016/j.mseb.2012.03.029

• Soft magnetic materials
• Composite materials
• Nanocrystalline materials
• Permeability
• Core loss

The preparation and characterization of the nanocrystalline soft magnetic composite core based on Supermalloy powder obtained via mechanical alloying route are presented. The AC magnetic properties of the compacts were determined in frequency range from 100 Hz to 100 kHz for flux densities of 0.05 and 0.1 T. Composite materials were obtained by covering the Supermalloy particles with a polymer binder, then compacted into toroidal shape and finally polymerized. It is found that an increase of the compacting pressure from 600 MPa to 800 MPa leads to an increase of the compacts permeability by more than 8%. Also, reducing the polymer content from 2 wt.% to 0.5 wt.% leads to an increase of the magnetic losses (at 100 kHz and 0.1T) by 380%. The removal of the stresses induced during compaction has been accomplished by a heat treatment at 170 degrees C for 120h. This leads to a significant increase (12%) of the relative initial permeability of the compacts.

• 出版日期2012-5-25