A novel thermal decomposition method for the synthesis of ZnO nanoparticles from low concentration ZnSO4 solutions

作者：Darezereshki Esmaeel^*; Alizadeh Mostafa; Bakhtiari Fereshteh; Schaffie Mahin; Ranjbar Mohammad

来源：Applied Clay Science, 2011, 54(1): 107-111.

DOI：10.1016/j.clay.2011.07.023

• Thermal decomposition method
• Zinc oxide
• Nanoparticles
• Synthesis

In this research work, ZnO nanoparticles were prepared by direct thermal decomposition method with Zn-4(SO4)(OH)(6)center dot 0.5H(2)O as a precursor. The precursor was calcinated in air for 1 h at 825 degrees C. Samples were characterized by X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), infrared spectrum (IR), and scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The XRD, EDS, and IR results indicated that the ZnO nanoparticles were pure. The average crystallite and particle size of the ZnO nanoparticles were estimated to be 87 nm and 92 nm by XRD and TEM, respectively. The SEM and TEM images showed that the ZnO nanoparticles were of spherical shape. The simplicity of the present method suggests its potential application at industrial scale as a cheap and convenient way to produce pure ZnO nanoparticles from low concentration ZnSO4 solutions.

• 出版日期2011-11