Luminescent properties of Gd3+ sensitized low-phonon energy CaGd4O7:Tb3+ green emitting novel phosphors

作者：Pavitra E; Yu Jae Su^*

来源：Ceramics International, 2013, 39(2): 1029-1036.

DOI：10.1016/j.ceramint.2012.07.023

• Sol gel processes
• CaGd4O7
• Luminescence properties
• Lifetime analysis

The trivalent terbium (Tb3+) ions activated CaGd4O7 (CG) phosphors were synthesized by a sol gel method. The characterizations were performed after the samples annealed at 1500 degrees C. The structural and morphological properties were analyzed from the X-ray diffraction patterns and scanning electron microscope images. The photoluminescence excitation spectra showed a broad-band between the wavelengths 250 and 300 nm, which were overlapped with the Gd3+ excitation bands. The photoluminescence spectra exhibited efficient green emission due to the sensitization effect of Gd3+ ions on the Tb3+ ions when exciting with the Gd3+ wavelength at 278 nm. In order to analyze the influence of Tb3+ concentration on the luminescence behavior of Tb3+ ions in the CG host lattice, the decay curves were measured. The temperature-dependent luminescence measurements were done to identify the thermal stability of CG:Tb3+ phosphors at elevated temperatures. The cathodoluminescent spectra also showed a similar behavior to that observed in PL spectra. The CIE chromaticity coordinates as a function of Tb3+ concentration were calculated and all the obtained chromaticity coordinates have been placed in the green spectral region.

• 出版日期2013-3