Ambient pressure dried shape-controllable sodium silicate based composite silica aerogel monoliths

作者：Shao Zaidong; He Xiaoyong; Niu Ziwei; Huang Teng; Cheng Xuan^*; Zhang Ying

来源：Materials Chemistry and Physics, 2015, 162: 346-353.

DOI：10.1016/j.matchemphys.2015.05.077

• Two-step surface modification
• Sodium silicate
• Ambient pressure drying
• Fiber reinforced
• Shape-controllable
• Thermal conductivity

The shape-controllable sodium silicate based fiber reinforced silica aerogel monoliths with excellent integrity and thermal insulating property were prepared by ambient pressure drying. The non-woven silica fiber up to 17.5 wt% could be uniformly distributed and well incorporated into the three-dimensional silica network since the fiber introduced and silica precursor could simultaneously react with methyltriethoxysilane (MTES) and trimethylchlorosilane (TMCS) during the two-step surface modification. The densities and porosities of the composite silica aerogel monoliths were 0.104-0.146 g/cm(3) and 93%-95%, respectively, with the thermal conductivities of 21-31 m W/(m K) and the average modulus of 323-535 kPa. The characteristic linear and zigzag responses were observed from the compression stress strain curves. Incomplete modification due to a large amount of fiber incorporation led to severe volume shrinkage during ambient pressure drying.

• 出版日期2015-7-15
• 单位厦门大学