Novel Composite Cermet for Low-Metal-Content Oxygen Separation Membranes

作者：Ruiz Trejo Enrique^*; Boldrin Paul; Lubin Alexandra; Tariq Farid; Fearn Sarah; Chater Richard; Cook Stuart N; Atkinson Alan; Gruar Robert I; Tighe Christopher J; Darr Jawwad; Brandon Nigel P

来源：Chemistry of Materials, 2014, 26(13): 3887-3895.

DOI：10.1021/cm501490n

A dense composite of silver and Ce0.8Sm0.2O2-delta (Ag-CSO) was manufactured from ceramic nanopartides coated by electroless deposition of silver. At 700 degrees C, a 1-mm-thick membrane of the composite delivered an excellent oxygen permeation rate from air with a value of 0.04 mu mol cm(-2) s(-1), using argon as the sweep gas and 0.17 mu mol cm(-2) s(-1) using hydrogen. The low sintering temperature of the CSO nanoparticles allows the use of Ag rather than Pt or Pd and reduces the amount of metal needed for electronic conductivity to just 5.6 vol 96, which is lower than any value reported in the literature. Oxygen diffusivity measurements confirmed that the oxygen migration remained high in the composite, with an increase in surface exchange coefficient of three orders of magnitude over Gd-doped ceria. The ease of membrane fabrication, combined with encouraging oxygen permeation rates, demonstrate the promise of the material for high-purity oxygen separation below 700 degrees C.

• 出版日期2014-7-8