A modified electroless route to monodisperse and uniform nickel nanoparticle

作者：Cheng Zhipeng; Xu Jiming^*; Zhong Hui; Song Juan

来源：Materials Chemistry and Physics, 2011, 131(1-2): 4-7.

DOI：10.1016/j.matchemphys.2011.09.034

• Nanostructures
• Chemical synthesis
• Electron microscopy
• Magnetic properties

Monodisperse and uniform nickel nanoparticles with an average diameter of similar to 30 nm were synthesized through a modified electroless route in which nickel hydroxide (Ni(OH)(2)) colloid, H(2)O/ethylene glycol (EG) mixing solution, and sodium hypophosphite were used as Ni source, solvent, and reducing agent, respectively. Different from the conventional electroless process, only a trace concentration of complexing agent, ethylenediaminetetraacetic acid (EDTA), was used in this route. At the optimum H(2)O/EG volume ratio, monodisperse nickel nanoparticles of high crystallinity were obtained. The presence of trace concentrations of EDTA is necessary for uniformity of the synthesized nickel nanoparticles. The formation process is discussed based on the experimental results.

• 出版日期2011-12-15
• 单位淮阴师范学院