An in situ study of the deposition of a calcium phosphate mineralized layer on a silicon-substituted hydroxyapatite sensor modulated by bovine serum albumin using QCM-D technology

作者：Dong, Gang; He, Liyong; Pang, Dongwen; Wei, Luxi; Deng, Chunlin^*

来源：Ceramics International, 2016, 42(16): 18648-18656.

DOI：10.1016/j.ceramint.2016.09.002

• Grain growth
• Interfaces
• Apatite
• Albumin adsorption
• QCM-D

The deposition of a calcium phosphate (Ca-P) mineralized layer on Si-HA surface (the blank group, Au and the control group, HA) with and without BSA preadsorption was observed in real time using a quartz crystal microbalance with dissipation (QCM-D) technique. The effect of silicon doping on the adsorption of BSA onto a HA sensor was investigated. Approximately 1.5-fold more BSA adsorbed onto HA than Si HA, indicating the inhibition of BSA adsorption onto the HA sensor by silicon doping. The decreasing Delta D-sat/Delta f(sat) value in the plots of Delta D-Delta f versus adsorption time was predominantly attributed to BSA adsorption, and the decreasing Delta D value with adsorption time during adsorption equilibrium could be explained by the structural rearrangement of BSA on different substrates. Specifically, BSA preadsorption could be a trigger for the formation of nucleation sites for the mineralized layer, promoting nucleation but inhibiting growth. The growth rate was greater on bare substrates than on BSA adsorption substrates. The growth rate of the mineralized layer on the adsorbed BSA layer depended on the substrates in the following manner: Au > Si-HA > HA. The morphology of the mineralized layer depended on the surfaces, and a greater number and a more uniform distribution of smaller nanoparticles were observed on surfaces with preadsorbed BSA. Therefore, BSA could modulate the growth of the mineralized layer at the interface, which is advantageous for fabricating advanced biomaterials.

• 出版日期2016-12
• 单位华南理工大学