Artificial mineral films similar to biogenic calcareous shells: oriented calcite nanorods on a self-standing polymer sheet

作者：Nagai Yuta; Oaki Yuya; Imai Hiroaki^*

来源：CrystEngComm, 2018, 20(12): 1656-1661.

DOI：10.1039/c7ce02143g

Micrometre-thick calcareous shells consisting of c-axis-oriented calcite nanorods are produced on an organic sheet as foraminiferal tests and isopod cornea cuticles. Here, we produced mineral films similar to biogenic calcareous shells on a self-standing polymer sheet in a supersaturated solution system by multistep crystal growth with the adjustment of the concentration ratio of poly.acrylic acid) (PAA) as a soluble controlling agent. In the initial stage, selective high-density nucleation was achieved at a relatively low PAA to calcium ion ratio (R = 1.0-1.2) to form of a calcite seed layer on the surface of conventional polyvinyl alcohol. Calcite nanorods elongated in the c direction were then grown perpendicularly to the seed layer in the progressive stages at a relatively high PAA ratio (R = 1.5-2.0). The artificial mineral films consisting of c-axis-oriented nanorods are suggested to exhibit mechanical properties similar to those of biogenic calcareous shells.

• 出版日期2018-3-28