Stability of the Ni-TiO2@nano CaO/Al2O3 complex catalyst used in ReSER process for hydrogen production

作者：Xu, Jia Yan; Xue, Xiao Chong; Wu, Su Fang^*

来源：International Journal of Hydrogen Energy, 2016, 41(16): 6781-6786.

DOI：10.1016/j.ijhydene.2016.03.070

• Hydrogen
• Adsorption
• Titanium dioxide
• Catalyst
• Stability

This paper describes the preparation and evaluation of a sorption complex catalyst of Ni-TiO2@nano CaO/Al2O3 for hydrogen production by a reactive sorption-enhanced reforming (ReSER) process. TiO2 coating-modified nano CaCO3 as the precursor of nano CaO was prepared by an adsorption phase technique which was able to strictly control the thickness and structure of surface to improve its durability. Ni-TiO2@nano CaO/Al2O3 was prepared by a mixing method which is general mixing that cannot control the content and structure of catalyst. The microstructure was tested by SEM and XRD, and variation in the sorption property of the catalyst was tested by thermogravimetric analysis (TGA). The results showed that TiO2 coating enhanced the stability of the sorption capacity of the catalyst. X-ray diffraction analysis revealed that the TiO2 coating modification inhibited the growth of Ni crystals and prevented CaO and Al2O3 from forming (CaO)(12)(Al2O3)(7) due to the physical isolation by the TiO2 coating of the nano CaCO3. Evaluation of the modified complex catalyst in the ReSER hydrogen production process revealed significant stability for 13 circulations.

• 出版日期2016-5-4
• 单位浙江大学