摘要
A exquisite structure of Nano-Pt Skin (NPS) with high catalytic activity for electrocatalytic oxidation of methanol was fabricated by an in-situ electrodeposition method. Bio-renewable carbonized wood chips (CWCs) ware acted as the precursor of substrate material for the electro. X-ray diffraction (XRD) pattern and scanning electron microscopy (SEM) indicated that the NPS had a high degree of Pt crystallinity. Electrocatalytic oxidation of methanol showed that there was a significant oxidation peak in the cyclic voltammetry (CV) of NPS/CWCs with a peak current density of 705 mA/cm(2). Compared with CWCs, the impedance of NPS/CWCs was small with fast electron transfer rate and had good stability. The unique structure of Nano-Pt Skin Coated Carbonized Wood Chips can be remarkably attributed to the increased activity for electrocatalytic oxidation of methanol at room temperature.
- 出版日期2018-3
- 单位江苏理工学院; 江苏大学