A water-born Zr-based porous coordination polymer: Modulated synthesis of Zr-fumarate MOF

作者：Zahn Gesa; Schulze Hendrik Albert; Lippke Jann; Koenig Sandra; Sazama Uta; Froeba Michael; Behrens Peter^*

来源：Microporous and Mesoporous Materials, 2015, 203: 186-194.

DOI：10.1016/j.micromeso.2014.10.034

• Metal-organic frameworks
• Water-based synthesis
• Microporous materials
• Modulation approach
• Zr-fumarate MOF

In this work, we present the water-based synthesis of the Zr-fumarate MOF (Zr-film MOF) by applying a monocarboxylic acid as modulator. The original synthesis of Zr-fum MOF was performed in a DMF-based batch at 120 degrees C. The product showed exceptional stability against aqueous solutions. Thus, a water-based synthesis seemed to be promising. Indeed, by adding various amounts of formic acid, acetic acid or propionic acid as modulator, respectively, highly crystalline Zr-film MOF can be obtained from water at 120 degrees C. The investigation of the influence of modulating molecules with different alkyl chain lengths showed that the particle size decreases when monocarboxylic acids with longer alkyl chains are used, e.g. acetic acid and propionic acid in comparison to formic acid. For the formation of the Zr-fum MOF synthesised with formic acid as modulator, the thermogravimetric and sorption behaviour as well as the stability against various solvents and pH values is discussed in detail. Furthermore, the Zr-turn MOF can also be obtained under very benign reaction conditions at room temperature from water, making this material interesting for various applications, for example as a biomaterial.

• 出版日期2015-2