Aluminium matrix tungsten aluminide and tungsten reinforced composites by solid-state diffusion mechanism

作者：Zhang, Hanzhu; Feng, Peizhong; Akhtar, Farid^*

来源：Scientific Reports, 2017, 7(1): 12391.

DOI：10.1038/s41598-017-12302-w

• REACTIVE SYNTHESIS
• HEATING RATE
• MICROSTRUCTURE
• KINETICS
• CRYSTALLIZATION
• FABRICATION
• POROSITY
• ALLOYS

In-situ processing of tungsten aluminide and tungsten reinforced aluminium matrix composites from elemental tungsten (W) and aluminium (Al) was investigated by thermal analysis and pulsed current processing (PCP). The formation mechanism of tungsten aluminides in 80 at.% Al-20 at.% W system was controlled by atomic diffusion. The particle size of W and Al in the starting powder mixture regulated the phase formation and microstructure. PCP of micron sized elemental Al and W resulted in formation of particulate reinforcements, W, Al4W and Al12W, dispersed in Al matrix. W particles were surrounded by a similar to 3 mu m thick dual-layer structure of Al12W and Al4W. The hardness of Al matrix, containing Al12W reinforcements, was increased by 50% compared to pure Al, from 0.3 GPa to 0.45 GPa and W reinforcements showed a hardness of 4.35 GPa. On PCP of 80 at.% Al-20 at.% W mixture with particle size of W and Al similar to 70 nm, resulted in formation of Al4W as major phase along with small fractions of Al5W and unreacted W phase. This suggested strongly that the particle size of the starting elemental Al and W could be the controlling parameter in processing and tailoring of phase evolution, microstructure of particulate reinforced Al matrix composite.

• 出版日期2017-9-28
• 单位中国矿业大学（北京）