Differential thermal and thermogravimetric analyses of bound water content in cellulosic substrates and its significance during cellulose hydrolysis by alkaline active fungal cellulases

作者：Vyas S; Pradhan SD; Pavaskar NR; Lachke A^*

来源：Applied Biochemistry and Biotechnology, 2004, 118(1-3): 177-188.

DOI：10.1385/ABAB:118:1-3:177

• cellulose
• endoglucanase
• differential thermal analysis
• thermogravimetry
• bound water
• vaporization

Various cellulosic substrates were examined for bound water content by differential thermal analysis (DTA) and thermogravimetry (TG). Samples were heated in the range of 30-100degreesC at a rate of 3degreesC/min. DTA vaporization curves for different cellulose samples indicated that the bound water (W-b) was vaporized at higher temperature than free water (W-f) at the surface. Weight loss was observed in two stages, corresponding to W-j and W-b in TG curves. The bound water content was dependent on the degree of crystallinity of cellulose. Among different cellulosic substrates, Walseth cellulose showed the highest bound water content, and it also was found to be the least crystalline. The alkaline-active, alkali-stable cellulase was obtained from the alkalotolerant Fusarium sp. The substrate specificity and viscometric characteristics confirmed the enzyme to be an endoglucanase. The W-b, content of Walseth cellulose was lowered during the enzymatic hydrolysis. The possible application of bound water analysis in understanding the hydrolysis of cellulosic substrates of different crystallinity is discussed.

• 出版日期2004-9