The profound effect of annealing on the electrospun poly(epsilon-caprolactone) scaffold is comprehensively investigated for the first time. Interestingly, after annealing at 42 degrees C, the contact angle of the sample decreases from (133.39 +/- 3.20) to (124.11 +/- 2.08)degrees, meanwhile the Young's modulus dramatically increases from 8.41 +/- 1.64 to 11.27 +/- 2.41 MPa, which is attributed to the improved crystallinity. The above results and additional excellent cellular proliferation demonstrate that the annealed matrix possesses better physical and biological performances as a tissue engineering scaffold.