A general, efficient method of incorporation of metal ions into ultrathin TiO2 films

作者：He JH; Ichinose I; Fujikawa S; Kunitake T^*; Nakao A

来源：Chemistry of Materials, 2002, 14(8): 3493-3500.

DOI：10.1021/cm010880w

A general, efficient method was developed to incorporate a variety of second metal ions into ultrathin TiO2 films. The thin films were first prepared by the surface sol-gel process from a mixture of the matrix-forming titanium alkoxide and template magnesium alkoxide. Mg2+ ion was removed by acid/base treatment, forming highly efficient and robust ion-exchange sites. A large variety of metal ions, including alkaline, alkaline earth, transition, and rare earth elements, were then incorporated into the thin films by ion exchange with Na+. The amount of incorporation increased with increasing charge of the metal ions. The rate of the ion-exchange process was investigated in the case of Gd3+. The incorporated metal ions were immobilized by thermal treatment at 450 degreesC. The UV absorption edge of the TiO2 film was extended to the visible region by Fe3+ doping and calcination.

• 出版日期2002-8
• 单位RIKEN