Highly conductive, optically transparent, low work-function hydrogen-doped boron-doped ZnO electrodes for efficient ITO-free polymer solar cells

作者：Polydorou Ermioni; Soultati Anastasia; Vasilopoulou Maria^*

来源：Journal of Materials Chemistry C, 2016, 4(4): 691-703.

DOI：10.1039/c5tc04001a

In this work, highly conductive, optically transparent and low work-function hydrogen-doped borondoped ZnO (BZO: H) cathode electrodes were prepared by a hydrogen post annealing treatment of the as-deposited boron-doped ZnO (BZO) samples. It was found that hydrogen post annealing at temperatures around 200 degrees C resulted in the formation of electrode materials which exhibited higher conductivity and carrier concentration, reduced sheet resistance and significantly increased optical transparency compared with their non-annealed BZO counterparts. In addition, hydrogen incorporation in the material lattice caused a significant reduction in their work function which may be beneficial for device operation. As a result, polymer solar cells using BZO: H films as transparent cathode electrodes exhibited higher efficiencies compared to those obtained for devices using the non-annealed counterparts. In particular, devices based on the poly(3-hexylthiophene) (P3HT):[6,6]-phenyl C(71)butyric acid methyl ester (PC71BM) system as the photoactive layer exhibited a PCE of 3.90%, whereas those based on the poly[(9-(1-octylnonyl)-9H-carbazole-2,7-diyl)-2,5-thiophenediyl-2,1,3-benzothiadiazole-4,7-diyl-2,5-thiophenediyl] (PCDTBT): PC71BM and poly[[4,8-bis[(2-ethylhexyl)oxy] benzo[1,2-b: 4,5-b'] dithiophene-2,6-diyl][3-fluoro-2-[(2-ethylhexyl) carbonyl]thieno[3,4-b] thiophenediyl]] (PTB7): PC71BM as the active components reached high PCE values of 5.90 and 7.25%, respectively, which are comparable or even higher than reported efficiencies obtained for devices using doped ZnO-based transparent electrodes.

• 出版日期2016