Alternating and Diblock Donor-Acceptor Conjugated Polymers Based on Diindeno[1,2-b:2 ',1 '-d]thiophene Structure: Synthesis, Characterization, and Photovoltaic Applications

作者：Chen Chiu Hsiang; Cheng Yen Ju^*; Dubosc Martin; Hsieh Chao Hsiang; Chu Cheng Che; Hsu Chain Shu

来源：Chemistry-An Asian Journal, 2010, 5(12): 2483-2492.

DOI：10.1002/asia.201000506

• copolymerization
• donor-acceptor systems
• photovoltaics
• polymers
• solar cells

Pentacyclic diindeno[1,2':2',1'-d]thiophene (DIDT) unit is a rigid and coplanar conjugated molecule. To the best of our knowledge, this attractive molecule has never been incorporated into a polymer and thus its application in polymer solar cells has never been explored. For the first time, we report the detailed synthesis of the tetra-alkylated DIDT molecule leading to its dibromo-and diboronic ester derivatives, which are the key monomers for preparation of DIDT-based polymers. Two donor-acceptor alternating polymers, poly(diindenothiophene-alt-benzothiadiazole) PDIDTBT and poly-(diindenothiophene-alt-dithienylbenzothiadiazole) PDIDTDTBT, were synthesized by using Suzuki polymerization. Copolymer PTDIDTTBT was also prepared by using Stille polymerization. Although PTDIDTTBT is prepared through a manner of random polymerization, we found that the different reactivities of the dibromo-monomers lead to the resulting polymer having a block copolymer arrangement. With the higher structural regularity, PTDIDTTBT, symbolized as (thiophene-alt-DIDT)(0.5)-block-(thiophene-alt-BT)(0.5), shows the higher degree of crystallization, stronger pi-pi stacking, and broader absorption spectrum in the solid state, as compared to its alternating PDIDTDTBT analogue. Bulk heterojunction photovoltaic cells based on ITO/PEDOT:PSS/polymer:PC71BM/Ca/Al configuration were fabricated and characterized. PDIDTDTBT/PC71BM and PTDIDTTBT/PC71BM systems exhibited promising power-conversion efficiencies (PCEs) of 1.65% and 2.00%, respectively. Owing to the complementary absorption spectra, as well as the compatible structures of PDIDTDTBT and PTDIDTTBT, the PCE of the device based on the ternary blend PDIDTDTBT/PTDIDTTBT/PC71BM was further improved to 2.40%.

• 出版日期2010