Development of a large area n-type PERT cell with high efficiency of 22% using industrially feasible technology

作者：Sheng, Jian; Wang, Wei; Yuan, Shengzhao; Cai, Wenhao; Sheng, Yun; Chen, Yifeng; Ding, Jiangning^*; Yuan, Ningyi^*; Feng, Zhiqiang; Verlinden, Pierre J.

来源：Solar Energy Materials and Solar Cells, 2016, 152: 59-64.

DOI：10.1016/j.solmat.2016.03.032

• N-type
• PERT
• Front junction
• High-efficiency
• Power loss analysis

A high-efficiency front junction n-type passivated emitter and a rear total diffusion (n-type PERT) solar cell with the front boron diffusion passivated by a Al2O3/SiNx stack layer deposited by plasma enhanced chemical vapor method and the rear with phosphorus total diffusion and Al evaporated local contact are presented in this paper. The main purpose of this study was to develop industrially feasible front junction n-type PERT solar cells with high-efficiency; these were realized on a large area of n-type industrial 5- and 6-in. wafers. An average of 21.85% cell efficiency was achieved on 5-in. wafers, and the highest cell convert efficiency of 21.98% was achieved with V-oc of 683.8 mV, J(sc) of 40.13 mA/cm(2), and FF of 80.11%. For 6-in. cells, we get Fraunhofer independently confirmed efficiency of 21.49% with a V-oc of 674.1 mV, a J(sc) of 39.77 mA/cm(2), a FF of 80.18%. Details of cell fabrication and results are presented, followed by a best cell power loss analysis on V-oc, I-sc and FF.

• 出版日期2016-8
• 单位常州大学; 江苏大学