Fabrication of visible-light active Fe2O3-GQDs/NF-TiO2 composite film with highly enhanced photoelectrocatalytic performance

作者：Wang, Qi; Zhu, Naxin; Liu, Engin; Zhang, Chenlu; Crittenden, John C.; Zhang, Yi; Cong, Yanqing^*

来源：Applied Catalysis B: Environmental , 2017, 205: 347-356.

DOI：10.1016/j.apcatb.2016.11.046

• Cr(VI) reduction
• NF-TiO2
• alpha-Fe2O3
• GQDs
• Photoelectrocatalytic

Visible-light active Fe2O3-GQDs/NF-TiO2 composite films were fabricated via sequential electrodeposition and electro-oxidation processes. The prepared photocatalytic films were extensively characterized using scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The results revealed that graphene quantum dots (GQDs) and alpha-Fe2O3 particles were simultaneously deposited onto the surface of N and F co-doped TiO2 (NF-TiO2) simply using a graphite sheet instead of a Pt sheet as anode in the electro-deposition process. The NF-TiO2 substrate obtained by calcining TiO2 nanotubes (TiO2-NTs) in the presence of NH4F displayed pyramid shapes with dominant (101) facets. Linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS) and Mott-Schottky (M-S) plots indicated that the generation, separation and transfer of photogenerated charges were greatly enhanced on the novel composite. The photocurrent density of Fe2O3-GQDs/NF-TiO2 was 4.2 times that on Fe2O3/TiO2-NTs at 0.5 V vs. Ag/AgCl under visible light irradiation. For the photoelectrocatalytic (PEC) reduction of Cr(VI) using Fe2O3-GQDs/NF-TiO2 as photoanode With a Ti sheet as cathode, substantially enhanced activity was achieved due to the combined effect of visible-light-active components (alpha-Fe2O3 and NF-TiO2) and excellent electron mediator (GQDs). The calculated reduction rate constant was 7 times that obtained on Fe2O3/TiO2-NTs film. Furthermore, both the long-time photocurrent and cyclic PEC reduction of Cr(VI) indicated good stability of the composite film.

• 出版日期2017-5-15
• 单位华东理工大学