A Simple, Quick and Eco-Friendly Strategy of Synthesis Nanosized alpha-LiFeO2 Cathode with Excellent Electrochemical Performance for Lithium-Ion Batteries

作者：Hu, Youzuo; Zhao, Hongyuan^*; Liu, Xingquan^*

来源：Materials, 2018, 11(7): 1176.

DOI：10.3390/ma11071176

• alpha-LiFeO2
• nanoparticle
• cathode material
• ambient temperature

Nanosized alpha-LiFeO2 samples were successfully synthesized via a simple, quick and eco-friendly strategy at ambient temperature followed by a low temperature calcined process. X-ray diffraction (XRD), scanning electronic microscopy (SEM) and transmission electron microscopy (TEM) measurements revealed that the optimal alpha-LiFeO2 sample was composed of extremely small nanoparticles. The electrochemical properties were tested at 0.1 C in the cut-off voltage of 1.5-4.8 V. The sample obtained at 150 degrees C for 6 h exhibited the best cycling stability with high initial discharge capacity of 223.2 mAh/g, which was extremely high for pristine alpha-LiFeO2 without any modification process. After 50 cycles, the discharge capacity could still maintain 194.5 mAh/g with good capacity retention. When the charge-discharge rate increased to 0.2 C and 0.5 C, the initial discharge capacities were 216.6 mAh/g and 171.5 mAh/g, respectively Furthermore, the optimal sample showed low charge transfer resistance and high lithium-ion diffusion coefficients, which facilitated the excellent electrochemical performance.

• 出版日期2018-7
• 单位电子科技大学