High-quality sandwiched black phosphorus heterostructure and its quantum oscillations

作者：Chen, Xiaolong; Wu, Yingying; Wu, Zefei; Han, Yu; Xu, Shuigang; Wang, Lin; Ye, Weiguang; Han, Tianyi; He, Yuheng; Cai, Yuan; Wang, Ning^*

来源：Nature Communications, 2015, 6(1): 7315.

DOI：10.1038/ncomms8315

• FIELD-EFFECT TRANSISTORS
• METAL-INSULATOR-TRANSITION
• MONOLAYER MOS2
• TRANSPORT-PROPERTIES
• MOBILITY
• OPTOELECTRONICS
• ELECTRONICS
• CRYSTALS
• CONTACT

Two-dimensional materials such as graphene and transition metal dichalcogenides have attracted great attention because of their rich physics and potential applications in next-generation nanoelectronic devices. The family of two-dimensional materials was recently joined by atomically thin black phosphorus which possesses high theoretical mobility and tunable bandgap structure. However, degradation of properties under atmospheric conditions and high-density charge traps in black phosphorus have largely limited its actual mobility thus hindering its future applications. Here, we report the fabrication of stable sandwiched heterostructures by encapsulating atomically thin black phosphorus between hexagonal boron nitride layers to realize ultra-clean interfaces that allow a high field-effect mobility of similar to 1,350 cm(2)V(-1) s(-1) at room temperature and on-off ratios exceeding 105. At low temperatures, the mobility even reaches similar to 2,700 cm(2)V(-1) s(-1) and quantum oscillations in black phosphorus two-dimensional hole gas are observed at low magnetic fields. Importantly, the sandwiched heterostructures ensure that the quality of black phosphorus remains high under ambient conditions.

• 出版日期2015-6