A Study of Hygrothermal Behavior of ACF Flip Chip Packages With Moire Interferometry

作者：Park Jin Hyoung^*; Jang Kyung Woon; Paik Kyung Wook; Lee Soon Bok

来源：IEEE Transactions on Components and Packaging Technologies, 2010, 33(1): 215-221.

DOI：10.1109/TCAPT.2009.2036154

• Anisotropic conductive film (ACF)
• coefficient of moisture expansion (CME)
• delamination
• electronic packaging
• Moire interferometry
• reliability

A primary factor of anisotropic conductive film (ACF) package failure is delamination between the chip and the adhesive at the edge of the chip. This delamination is mainly affected by the thermal shear strain at the edge of the chip. This shear strain was measured on various electronic ACF package specimens by micro-Moire interferometry with a phase shifting method. In order to find the effect of moisture, the reliability performance of an adhesive flip-chip in the moisture environment was investigated. The failure modes were found to be interfacial delamination and bump/pad opening which may eventually lead to total loss of electrical contact. Different geometric size specimens in terms of interconnections were discussed in the context of the significance of mismatch in coefficient of moisture expansion (CME) between the adhesive and other components in the package, which induces hygroscopic swelling stress. The effect of moisture diffusion in the package and the CME mismatch were also evaluated by using the Moire interferometry. From Moire measurement results, we could also obtain the stress intensity factor K. Through an analysis of deformations induced by thermal and moisture environments, a damage model for an adhesive flip-chip package is proposed.

• 出版日期2010-3