Limiting factors for low-temperature performance of electrolytes in LiFePO4/Li and graphite/Li half cells

作者：Li, Jie; Yuan, Chang Fu; Guo, Zhi Hong; Zhang, Zhi An; Lai, Yan Qing; Liu, Jin^*

来源：Electrochimica Acta, 2012, 59: 69-74.

DOI：10.1016/j.electacta.2011.10.041

• Li-ion battery
• Low temperature
• Electrolyte
• LiBF4
• LiPF6

Low-temperature performance of LiBF4 and LiPF6-based electrolytes in LiFePO4/Li and graphite/Li half cells was investigated. In the temperature range from 0 degrees C to -40 degrees C, electrochemical impedance spectroscopy (EIS) results show that the charge-transfer resistance (R-ct) of graphite/Li cell decreases, the R-ct of LiFePO4/Li cell increases, and sum resistance of LiFePO4/Li and graphite/Li cell decreases when replacing LiPF6 with LiBF4. In the temperature range from 25 degrees C to -40 degrees C, energy barrier (W) for Li-ion jump at the solid electrolyte interface (SEI) alters slightly from 16.04 kJ/mol to 13.60 kJ/mol in LiFePO4/Li cells, but declines greatly from 46.47 kJ/mot to 19.81 kJ/mol in graphite/Li cells when using LiBF4 instead of LiPF6, meanwhile, activation energy (Delta G) of electrode reaction is approximately the same (similar to 60 kJ/mol). The above results indicate that the ionic conductivity is the main limiting factor for low-temperature performance of electrolytes in LiFePO4/Li cell, while factors related with electrolyte-interface are more crucial in graphite/Li cell than in LiFePO4/Li cell.

• 出版日期2012-1-1
• 单位中南大学