摘要
A (ferrite + carbide) microduplex structure formed by dynamic recrystallization of ferrite during warm deformation of martensite was found to exhibit superplastic characteristics. The value of m = 0.4 was obtained at 973 K and a strain rate of 10(-4) s(-1). Microstructural analysis shows that submicron carbides are located at the ferrite grain boundary, while nanometer ones are dispersed inside ferrite grains. This kind of carbide distributi
- 出版日期2010-5
- 单位清华大学