A graphene-supported copper-based catalyst for the hydrogenation of carbon dioxide to form methanol

作者：Fan, Yu Jia; Wu, Su Fang^*

来源：Journal of CO2 Utilization, 2016, 16: 150-156.

DOI：10.1016/j.jcou.2016.07.001

• Reduced graphene oxide
• Methanol
• Carbon dioxide
• Copper-based catalyst
• Adsorption

The use of reduced graphene oxide (rGO) as a novel support for the CuO-ZnO-ZrO2-Al2O3/rGO (CZZA/rGO) catalyst in forming methanol by carbon dioxide hydrogenation has been studied herein. Furthermore, the CuO-ZnO-ZrO2-Al2O3 (CZZA) catalyst was also prepared to compare catalytic performance. The catalysts were characterized using BET specific surface area, X-ray diffraction (XRD), H-2-temperature programmed reduction (H-2-TPR), scanning electron microscopy (SEM), H-2-temperature-programmed desorption (H-2-TPD) and CO2-temperature-programmed desorption (CO2-TPD) techniques and were evaluated by a fixed-bed reactor for methanol synthesis from the hydrogenation of carbon dioxide. The characterization results show that the surface area of the CZZA/rGO catalyst was 125.6 m(2)/g and the adsorption capacity of H-2 and CO2 increased remarkably due to the support of rGO. Moreover, the CO2 conversion over the CZZA/rGO catalyst was 14.7% under optimum reaction conditions (a temperature of 513 K, a pressure of 20 bar, and a space velocity of 6075h(-1)). The methanol yield was 11.6%, while that of CZZA catalyst without rGO support was only 9.8%. The superior activity of the CZZA/rGO catalyst could be attributed to its large surface area and high H-2 and CO2 adsorption capacity, which prevent the catalyst sintering and led to a higher CO2 conversion and methanol selectivity.

• 出版日期2016-12
• 单位浙江大学