Using X-ray microtomography to evaluate cavity formation in a superplastic magnesium alloy processed by equal-channel angular pressing

作者：Figueiredo Roberto B^*; Terzi Sofiane; Langdon Terence G

来源：Acta Materialia, 2010, 58(17): 5737-5748.

DOI：10.1016/j.actamat.2010.06.049

• Cavitation
• Equal-channel angular pressing
• Magnesium alloys
• Superplasticity
• X-ray microtomography

The magnesium AZ31 alloy exhibits excellent superplastic properties after processing by equal-channel angular pressing (ECAP) and testing in tension at a temperature of 623 K. Experiments show that there is an increase in the elongations to failure with increasing numbers of passes in ECAP. X-ray microtomography was used to obtain detailed information on the morphologies of cavities developed during superplastic flow and the results were analyzed in terms of the different possible cavity growth mechanisms. The results show that superplastic elongations are attained in this alloy because the finer grain structure introduced by ECAP is associated with lower flow stresses in tensile testing at elevated temperatures and this leads to a reduction in the rate of growth of internal cavities.

• 出版日期2010-10