A novel approach to synthesis of high-dispersed anatase titania nanocrystals

作者：Hari Bala; Zhao JZ; Jiang YQ; Ding XF; Tian YM; Yu KF; Wang ZC^*

来源：Materials Letters, 2005, 59(14-15): 1937-1940.

DOI：10.1016/j.matlet.2005.02.030

• anatase titania
• high-dispersed
• nanocrystals
• needle-shape
• sol-gel process
• forming solid substrates

A novel approach was employed in the synthesis of high-dispersed anatase titania (TiO2) nanocrystals by sol-gel process with NH4NO3 (AN) as solid substrates. Further calcination was conducted after the hydrous TiO2 nanoparticles were adsorbed onto the surface of AN particles. The products were investigated by TGA, XRD, and TEM. The results indicated that AN was melting and decomposing during the calcining process, which was very important to inhibit the agglomeration of anatase TiO2 nanocrystals. The highly dispersed anatase TiO2 nanocrystals were in needle-shape having lengths about 16-20 nm and diameter of 6-9 nm.

• 出版日期2005-6
• 单位吉林大学