A constitutive model for dynamic plasticity of FCC metals

作者：Gao C Y; Zhang L C

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2010, 527(13-14): 3138-3143.

DOI：10.1016/j.msea.2010.01.083

• Constitutive relation
• Plastic deformation
• Dislocation mechanisms
• OFHC copper
• High strain rate
• Large strain

This paper proposes a new constitutive model to describe the dynamic plasticity of FCC metals using the thermal activation mechanism of dislocation motion. In the model development, the constitutive parameters were directly linked with the characteristics of microstructures of materials. As an example of its application, the model was used to describe the behavior of OFHC copper. To determine the globally optimized parameters of the constitutive model for OFHC copper, an improved multi-variable optimization method of constrained nonlinear programming was used based on the flow stress of the material measured experimentally. A comparison with some models and experimental data in the literature shows that the new model is simple to apply and is much better in terms of its prediction accuracy. It was shown that compared with the MTS model the new constitutive equation is explicit and can be easily embedded into a computational code of material dynamics; while compared with the Zerilli-Armstrong and Johnson-Cook models the new one reflects more precisely experimental observations. It was concluded that the new model is applicable to a wide range of problems with temperature variation from 77K to 1096K, strain rates ranging from 10(-3) s(-1) to 104 s(-1), and strain as high as 1.

• 出版日期2010-5-25
• 单位浙江大学