摘要
The microhardness of chalcogenide glasses (ChGs) of the Sn-Sb-Se (SSS) ternary system was investigated, and the correlation of microhardness with the mean coordination number of the SSS ChGs was determined. To prepare infrared-transparent SSS glass-ceramics (GCs), two SSS ChGs (A, Sn6.23Sb14.11Se79.66; B, Sn9.8Sb17.22Se72.98; by molar composition) were selected and thermally treated at 433 and 448 K, respectively. The improved microhardness (with values that increased by 11.5% and 7.3% for SSS ChG A and B, respectively) of the resulting SSS GCs is attributed to the formation of Sb2Se3 nanocrystals.
- 出版日期2019-4
- 单位宁波大学