Dual functionality of PTSA as electrolyte and dopant in the electrochemical synthesis of polyaniline, and its effect on electrical properties

作者：Bhadra Sambhu; Singha Nikhil K; Khastgir Dipak^*

来源：Polymer International, 2007, 56(7): 919-927.

DOI：10.1002/PI.2225

• polyaniline
• conductivity
• electrochemical synthesis
• dielectric properties

The electrochemical synthesis of polyaniline (PAni) powder was carried out from an aqueous solution of 0.15 mol L-1 aniline with varying concentrations of p-toluenesulphonic acid (PTSA) at room temperature. The PAni samples thus obtained were characterized using DC and AC conductivity, dielectric properties, infrared spectroscopy, thermogravimetric analysis, X-ray analysis, scanning electron microscopy and ultraviolet spectroscopy. Results showed that PTSA is acting both as electrolyte and doping agent. With an increase in the PTSA concentration, there is more polaron formation, and this means an increase in charge carrier concentration and mobility. This accounts for the increase in conductivity and improved dielectric properties of the resultant PAni. The polymer was subjected to a heating and cooling cycle. The change in conductivity during the heating cycle is quite different from that during the cooling cycle, indicating some kind of hysteresis phenomenon occurring in the system. Moreover there is a net decrease in room temperature conductivity of PAni when subjected to the heating-cooling cycle. This may be due to the oxidation of PAni and generation of some kind of disorder in the structure of PAni during the heating-cooling process.

• 出版日期2007-7