Adhesive properties of modified triticale distillers grain proteins

作者：Bandara Nandika; Chen Lingyun; Wu Jianping^*

来源：International Journal of Adhesion and Adhesives, 2013, 44: 122-129.

DOI：10.1016/j.ijadhadh.2013.02.014

• Triticale distillers grain protein
• Adhesion strength
• Protein modification
• Water resistance properties

The adhesive properties of five protein extracts (DDGSae, DWGae, DDGSaa, DWGaa, and P6L) from triticale distillers grain were studied with/without modifications using 0.5 mM NaOH, 1 M urea or 60 mu M glutaraldehyde. The dry, wet and soaked adhesion strength was measured using an automated bonding evaluation system (ABES II). The highest (p < 0.05) adhesion strength was observed for acetic acid extracted proteins in all modifications. Among three different modifications, glutaraldehyde modification exhibited the greatest improvement. Glutaraldehyde modification increased the adhesion strength of DDGSaa from 2.56, 0.84, 1.11 MPa to 3.86, 2.03, 2.60 MPa for dry, wet and soaked adhesion strength, respectively. Increase in alpha-helical conformation and molecular weight was observed for glutaraldehyde modified proteins according FTIR and SDS-PAGE results.

• 出版日期2013-7